How to Choose Refractory Brick for Cement Kiln

As the market’s requirements for cement production efficiency and quality increase, it is extremely important to select refractory bricks for cement kilns. Because this means that the operation speed of cement kilns will continue to accelerate, and the operating temperature of the kiln will also continue to increase. When running this project, you are better off choosing refractory bricks that will last longer.

Main Kinds of Refractory Bricks for Cement Kiln

1. Alumina Silicon Carbide Brick
  • Features: good thermal stability, high mechanical strength, good abrasion strength;
  • Application Area: transition zone of cement kiln;

2. Dolomite Brick
  • Features: good hanging kiln skin performance, good corrosion resistance;
  • Application: suitable for lining of cement kiln;

3. Magnesia Chrome Brick
  • Features: good hanging kiln skin performance, high working temperature;
  • Application: suitable for sintering zone of cement kiln;

4. Magnesia Alumina Spinel Brick
  • Features: good thermal shock resistance, good oxide reducibility, good resistance to peeling;
  • Application: suitable for transition zone of cement kiln;

5. High Alumina Brick
  • Features: high working temperature, good chemical resistance, long service life;
  • Application: suitable for sintering zone of cement kiln;

6. Silicon Carbide Brick
  • Features: high working temperature, low thermal expansion, good thermal shock resistance;
  • Application: suitable for cooling zone and entrance of cement kiln;

7. Phosphate Brick
  • Features: strong resistance to alkaline and other substances, good resistance to slag;
  • Application: suitable for inner lining of cement kiln;

8. Other Refractory Bricks
  • Features: wide selection, support customization, superior quality and performance;
  • Application: suitable to be used in all areas of cement kiln.

Main Reasons That Cause Corrosion to Refractory Bricks

Alkali and Salt Corrosion

The alkali salt compounds in the cement kiln will penetrate into the refractory bricks and form a horizontal penetration layer inside the refractory bricks. The formation of this chemical is inconsistent with the performance of the original refractory bricks. Therefore, it is easy to fall off when faced with high temperature impact. You can observe the operating conditions inside the kiln in time. Generally speaking, the color changes of the layered refractory bricks are more obvious. When selecting refractory bricks, attention should be paid to low porosity and impurities.

Oxidation Effect

As the oxidizing atmosphere and reducing atmosphere inside the cement kiln fluctuate, volume changes and structural spalling will occur as a whole. Refractory bricks containing iron elements are greatly affected. Because when this product faces reduction reaction, the working surface will turn white or the non-working surface will turn black. This in turn causes the brick structure to burst. Customers can contact the supplier to adjust the proportion of iron elements in the refractory bricks to effectively solve the damage caused by oxidation and reduction.


Hydration Cracks

During the operation of the cement kiln, hydration cracks may also occur. The specific manifestation is that the surface of the refractory bricks will turn white and if the degree of hydration is large, it may also appear spider web-like fragmentation. The main reason for this factor is that MgO reacts with H2O in the air to form Mg(OH)2, and the increase in volume causes cracking of the firebrick. In order to prevent hydration cracks of refractory bricks, when storing refractory bricks, they must be stored dry indoors.

Mechanical Corrosion

Cement kilns bear comprehensive pressure during operation. Because the cylinder is elliptical and extrusion and twisting will occur between the high temperature refractory bricks. In addition, the cement kiln also experiences strong thermal shock during operation, which will inevitably lead to bending and deformation of the cylinder. Therefore, when customers choose refractory bricks, it is best to choose ones with lower porosity and expansion coefficient.

Conclusion

Kerui offers a basic guide about how to choose refractory bricks for cement kiln. For customers who operate high temperature cement kiln, welcome to select suitable refractory bricks as well as other refractory and insulation materials from Kerui Refractory company. We’re confident to provide high quality products and perfect solution!

    Contact Us

    Please feel free to give your inquiry in the form below. We will reply you right now! Email: market@krref.com

    * Name:

    * Email:

    Phone/Whatsapp (including area code):

    * Message: Please leave the following information for quicker reply: product name, specifications, dimension/ drawing, quantity, usage, etc.

  • GET PRICE
    X GET PRICE

      Contact Us

      Please feel free to give your inquiry in the form below. We will reply you right now! Email: market@krref.com

      * Name:

      * Email:

      Phone/Whatsapp (including area code):

      * Message: Please leave the following information for quicker reply: product name, specifications, dimension/ drawing, quantity, usage, etc.